Web本研究藉由表面修飾來改變二硫化鉬的光學和電學特性,利用羅丹明B(Rhodamin B, RhB)和二甲基甲醯胺(DMF)修飾二硫化鉬有效地達到與二硫化鉬的電荷轉移,並探討RhB和DMF的電荷轉移機制。利用拉曼光譜(Raman)和光致螢光光譜(Photoluminescence)檢視RhB和DMF修飾對二硫化鉬造成P型摻雜或和型摻雜的效果;利用 ... WebDec 15, 2024 · A 532 nm laser was used for Raman characterization and photocurrent mapping on a piezo-crystal-controlled scanning stage. The scanning transmission …
MoSe2–Cu2S Vertical p–n Nanoheterostructures for High …
WebApr 6, 2024 · A linear correlation between the photocurrent measured electrochemically on Cu ... The co-electrodeposition of copper and indium from a pH 3 tartrate bath onto 4.8 … WebPlease login to get the full event experience. Login. Welcome Spring 2024 ; Lobby ddds7 アルパイン
Fully Depleted Self-Aligned Heterosandwiched Van Der Waals ...
WebAug 30, 2024 · We investigate the excitonic transitions in single- and few-layer MoSe2 phototransistors by photocurrent spectroscopy. The measured spectral profiles show a well-defined peak at the optically active (bright) A0 exciton resonance. More interestingly, when a gate voltage is applied to the MoSe2 to bring its Fermi level near the bottom of … WebJan 24, 2024 · Here, the 920 nm (1.35 eV) photons lie below the band gaps and produce very little photocurrent in the constituent monolayer materials but resonantly excite the interlayer optical transition in the heterostructure, producing a 5-fold enhancement in the measured photocurrent.}, doi = {10.1021/acsanm.9b01898}, journal = {ACS Applied … WebOct 9, 2024 · The photoresponsivity and normalized photocurrent‐to‐dark current ratio reach up to 127 mA W−1 and 1.9 × 104 mW−1, respectively. The results not only provide … dddriver 不明なデバイス